Top Body Ball Clay
| PHYSICAL PROPERTIES | CHEMICAL ANALYSIS | ||
| NAME OF TEST | RESULT | COMPOUND | RESULT % |
| SHRINKAGE % | 13.05 | SiO2 % | 53.35 |
| LOSS ON IGNITION % | 11.54 | AI2O3 % | 30.56 |
| DRY M.O.R kg/cm ² | 28.7 | Fe203 % | 1.13 |
| FIRE M.O.R kg/cm ² | 254.8 | TiO2 % | 1.49 |
| WATER ABSORPTION % | 6.85 | CaO % | 0.28 |
| WATER OF PLASTICITY % | 35.6 | MgO % | 0.41 |
| T.D.S | 330 | K2O % | 0.42 |
| RESIDUE (240 # 2 Minute Grinding) | 0.72 | Na2O % | 0.32 |
| L * | 86.71 | Loss On Ignition % | 11.75 |
| NAME OF TEST | MIX 75 | ||
| a * | 2.16 | Shrinkage % | 10.04 |
| b * | 11.61 | L * | 78.91 |
| WHITENESS | 68.97 | a * | 1.55 |
| TEMPRATURE C | 1195/1205 | b * | 13.17 |
| CYCLE MIN. | 55 | Whiteness | 54.8 |